Multi-modal shape memory polymers

ABSTRACT

The present disclosure relates to a multi-modal shape memory polymer material comprising a blend of at least one polymer component having a first molecular weight and at least a second polymer component having a second molecular weight that is less than the first component.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a U.S. National Stage Application, submitted under 35 U.S.C. 371, claiming priority to PCT International Patent Application PCT/US2008/060783 filed on Apr. 18, 2008, which claims priority to U.S. Patent Application No. 60/912,827 filed on Apr. 19, 2007, the disclosures of which are incorporated herein by reference in their entirety.

BACKGROUND

1. Field of the Invention

This present disclosure relates generally to shape memory polymers and, more particularly, multi-modal shape memory polymers.

2. Related Art

Amorphous orientated shape memory polymers containing single molecular weight distributions are known to relax and form fixation devices when placed into a bone cavity. Upon observation, these shape memory polymer materials relax and try to flow into the small pores of bone. Polymers used for current shape memory applications have molecular weight distributions of polydispersity in the range of between about 2 to about 4. These types of ranges may limit the ability of the polymer to penetrate into the bone, the mechanical properties of the polymer itself, or in the case where the polymer is resorbable, the degradation time of the polymers.

SUMMARY

In an aspect, the present disclosure relates to a multi-modal shape memory polymer material comprising a blend of at least one polymer component having a first molecular weight and at least a second polymer component having a second molecular weight that is less than the first component. In an embodiment, the polymer material is bi-modal. In another embodiment, the first molecular weight has an M_(n) in excess of about 30,000 Daltons and the second molecular weight has an M_(n) of up to about 30,000 Daltons. In yet another embodiment, the first molecular weight has an M_(n) of between about 50,000 and about 1,000,000 Daltons and the second molecular weight has an M_(n) of between about 2,000 and about 30,000 Daltons. In a further embodiment, the at least one polymer component comprises about 80% of the polymer blend and the second polymer component comprises about 20% of the polymer blend.

In an embodiment, the at least one polymer component and the second polymer component are both resorbable. In another embodiment, the at least one polymer component and the second polymer component are both non-resorbable. In yet another embodiment, one of the at least one polymer component and the second polymer component is resorbable and one of the at least one polymer component and the second polymer component is non-resorbable. In a further embodiment, both of the components are miscible. In yet a further embodiment, the material includes a filler selected from a group consisting essentially of hydroxyapatite, calcium carbonate, and tricalcium phosphate.

In an embodiment, the material includes a porogen selected from a group consisting essentially of sodium chloride, lithium bromide, lithium iodide, calcium chloride, sodium iodide, magnesium sulphate, and calcium sulphate. In another embodiment, at least one or both of the at least one polymer component and the second polymer component includes a polyester selected from a group including P(L)LA, poly(D)lactic acid (P(D)LA), poly(DL)lactic acid (P(DL)LA), poly(L-co-DL)lactic acid (P(LDL)LA), poly(L)lactic acid-co-glycolide (P(L)LGA)), poly(DL)lactic acid-co-glycolide (P(DL)LGA)), poly(D)lactic acid-co-glycolide (P(D)LGA)), polycaprolactone (PCL), PGA, and combinations thereof.

In yet another embodiment, at least one or both of the at least one polymer component and the second polymer component includes a polyacrylate. In a further embodiment, at least one or both of the at least one polymer component and the second polymer component includes a polymethyl methacrylate polymer or copolymer thereof. In yet a further embodiment, at least one or both of the at least one polymer component and the second polymer component includes a polybutyl methacrylate polymer or copolymer thereof. In an embodiment, at least one or both of the at least one polymer component and the second polymer component includes a polybutyl methacrylate-co-polymethyl methacrylate copolymer. In another embodiment, at least one or both of the at least one polymer component and the second polymer component includes a polystyrene copolymer.

In another aspect, the present disclosure relates to an article comprising a multi-modal shape memory polymer material comprising a blend of at least one polymer component having a first molecular weight and at least a second polymer component having a second molecular weight that is less than the first component. The article is selected from a group consisting essentially of rods, pins, nails, screws, plates, anchors, and wedges.

In a further aspect, the present disclosure relates to the use of the article as a fixation device suitable for implantation into bone wherein upon implanting the article into bone and providing the article with energy, the material flows into pores of the bone thereby enhancing fixation of the article to bone.

In yet a further aspect, the present disclosure relates to an article comprising a multi-modal shape memory polymer material comprising a blend of at least one polymer component having a first molecular weight and at least a second polymer component having a second molecular weight that is less than the first component, wherein upon implanting the article into bone and providing the article with energy, the material flows into pores of the bone thereby enhancing fixation of the article to bone.

Further features, aspects, and advantages of the present disclosure, as well as the structure and operation of various embodiments of the present disclosure, are described in detail below with reference to the accompanying drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

The accompanying drawings, which are incorporated in and form a part of the specification, illustrate the embodiments of the present disclosure and together with the description, serve to explain the principles of the disclosure. In the drawings:

FIG. 1 is an overlayed chromatograph showing the molecular weight profile distribution of a monomodal polymer material and the multi-modal polymer material of the present disclosure.

FIG. 2 is a chromatograph showing the molecular weight profile distribution of the multi-modal polymer material of the present disclosure.

DETAILED DESCRIPTION OF THE EMBODIMENTS

The following description of the preferred embodiments) is merely exemplary in nature and is in no way intended to limit the disclosure, its application, or uses.

The present disclosure relates to a multi-modal shape memory polymer material comprising a blend of at least one polymer component having a first molecular weight and at least a second polymer component having a second molecular weight that is less than the first component.

The first polymer component represents about 80% of the polymer blend and includes a high molecular weight having an M_(n) in excess of about 30,000 Daltons, and in some embodiments, between about 50,000 and about 1,000,000 Dollops. The second component represents about 20% of the polymer blend and includes a low molecular weight having an M_(n) of up to about 30,000 Daltons, and in some embodiments, between about 2,000 and about 30,000 Daltons. The high molecular weight of the first component provides the blend with the necessary mechanical strength and the low molecular weight of the second component provides the blend with the necessary flow characteristics and therefore the necessary amount of integration of the blend into bone, as will be further described below.

For the purposes of this disclosure, both the first and second polymer components include a polylactide based shape memory polymer. However, the polymer material may include a resorbable and/or non-resorbable polymer material having shape-memory qualities and which is selected from a group that includes an amorphous polymer, a semi-crystalline polymer, and combinations thereof.

Specific polymers that may be used include polyacrylic/polyacrylate, polymethyl methacrylate (PMMA), polyethyl methacrylate (PEMA), polybutylacrylate, polybutylmethacrylate, polystyrene, poly-alpha-hydroxy acids, polycaprolactones, polydioxanones, polyesters, polyglycolic acid, polyglycols, polylactides, polyorthoesters, polyphosphates, polyoxaesters, polyphosphoesters, polyphosphonates, polysaccharides, polytyrosine carbonates, polyurethanes, and copolymers or polymer blends thereof. Also, the polymer components may be miscible and capable of forming a substantially uniform blend. Polyesters that may be used include P(L)LA, poly(D)lactic acid (P(D)LA), poly(DL)lactic acid (P(DL)LA), poly(L-co-DL)lactic acid (P(LDL)LA), poly(L)lactic acid-co-glycolide (P(L)LGA)), poly(DL)lactic acid-co-glycolide (P(DL)LGA)), poly(D)lactic acid-co-glycolide (P(D)LGA)), polycaprolactone (PCL), PGA, and combinations thereof.

Generally, polymers that display shape memory qualities show a large change in modulus of elasticity at the glass transition temperature (T_(g)). The shape-memory function can be achieved by taking advantage of this characteristic. Namely, the mixture of the first and second polymer components is processed, via processes known to one of skill in the art, to make an article having a definite shape (the original shape). The article is then processed to give the article a secondary shape and to provide the article with shape memory qualities The process may process include, without limitation, die drawing, zone drawing, hydrostatic extrusion, compression flow molding, thermoforming, rolling, and roll drawing. The article is then softened by providing the article with energy and heating to a temperature (T_(f)) higher than the T_(g) of the polymer, but lower than the melting temperature (T_(m)) thereof so as to deform the article back to its original shape.

The article may include fixation devices, such as, without limitation, rods, pins, intramedullary nails, bone screws, locking screws, plates, anchors, staples, and wedges, for use in the repair of bone and soft tissue. In addition, the article may include a sleeve of polymer material, including a central channel, which allows the sleeve to be placed on a fixation device, such as the fixation devices listed above, for subsequent use in fixating the fixation device to bone, as is described in PCT International Application Publication WO2008/112875, the disclosure of which is incorporated herein by reference in its entirety.

Examples of adding energy to the polymer material include electrical and thermal energy sources, the use of force, or mechanical energy, and/or a solvent. The thermal energy source may include a heated liquid, such as water or saline. It is also within the scope of this disclosure that once the macroscopic body is placed in the bone, body heat would be transferred from blood and tissue, via thermal conduction, to provide the energy necessary to deform the shape memory polymer material. In this instance, body temperature would be used as the thermal energy source. Examples of electrical energy sources include heat generating devices such as a cauterizing device or insulated conductor, as more fully described in the ‘828 application, or a heating probe, as more fully described in PCT International Application Publication WO2008/112880, the disclosure of which is incorporated herein by reference in its entirety.

Any suitable force that can be applied either preoperatively or intra-operatively can be used. One example includes the use of ultra sonic devices, which can relax the polymer material with minimal heat generation. Solvents that could be used include organic-based solvents and aqueous-based solvents, including body fluids. Care should be taken that the selected solvent is not contra indicated for the patient, particularly when the solvent is used intra-operatively. The choice of solvents will also be selected based upon the material to be relaxed. Examples of solvents that can be used to relax the polymer material include alcohols, glycols, glycol ethers, oils, fatty acids, acetates, acetylenes, ketones, aromatic hydrocarbon solvents, and chlorinated solvents.

The article may include a composite or matrix having reinforcing material or phases such as glass fibers, carbon fibers, polymeric fibers, ceramic fibers, ceramic particulates, rods, platelets, and fillers. The fillers may include osteoconductive materials and/or biological actives such as, without limitation, hydroxyapatite, calcium carbonate, and tricalcium phosphate. Other reinforcing material or phases known to one of ordinary skill in the art may also be used. In addition, the polymeric material may be made porous via the use of porogens. The porogens include, without limitation, sodium chloride, lithium bromide, lithium iodide, calcium chloride, sodium iodide, magnesium sulphate, and calcium sulphate. Porosity may allow infiltration by cells from surrounding tissues, thereby enhancing the integration of the material to the tissue.

Also, one or more active agents may be incorporated into the material. Suitable active agents include bone morphogenic proteins, antibiotics, anti-inflammatories, angiogenic factors, osteogenic factors, monobutyrin, thrombin, modified proteins, platelet rich plasma/solution, platelet poor plasma/solution, bone marrow aspirate, and any cells sourced from flora or fauna, such as living cells, preserved cells, dormant cells, and dead cells. It will be appreciated that other bioactive agents known to one of ordinary skill in the art may also be used. Preferably, the active agent is incorporated into the polymeric shape memory material, to be released during the relaxation or degradation of the polymer material. Advantageously, the incorporation of an active agent can act to combat infection at the site of implantation and/or to promote new tissue growth.

EXAMPLE

A bimodal polymer blend, as described above, was prepared by compounding a mixture containing 35% w/w CaCO3, 6.5% w/w Poly(DL-Lactide) (MLA) (molecular weight, M_(n)=13900, M_(w)=20500) and 58.5% w/w Poly(L-co-DL-Lactide) 70:30 (PLDLA) (molecular weight, M_(n)=354700, M_(w)=854500) using a twin screw extruder. The resulting material was moulded to produce a 30 mm diameter rod suitable for die drawing. The rod was drawn through a 15 mm die at 75° C. at a rate of 20 mm/minute to produce a rod with a diameter of about 15 mm. The rod included shape memory qualities. The resulting rod was machined to produce plugs of 25 mm in length and 13 mm in diameter. Each plug also included an 8 mm diameter central opening. A stainless steel sleeve having a 4 mm diameter central opening was then press fitted into the central opening of each plug. The sleeve had a length of 25 mm and a diameter of 13 mm.

A monomodal polymer blend, to be used for control purposes, was prepared by compounding a mixture containing 35% w/w CaCO3, 65% w/w Poly(L-co-DL-Lactide) 70:30 (PLDLA) (molecular weight, M_(n)=354700, M_(w)=854500) using a twin screw extruder. The resulting material was molded to produce a 30 mm diameter rod suitable for die drawing. The rod was drawn through a 15 mm die at 75° C. at a rate of 20 mm/minute to produce a rod with a diameter of approximately 15 mm. The rod included shape memory qualities. Each plug also included an 8 mm diameter central opening. A stainless steel sleeve having a 4 mm diameter central opening was then press fitted into the central opening of each plug. The sleeve had a length of 25 mm and a diameter of 13 mm.

The molecular weight of both the monomodal and the bimodal polymer blends was determined using gel permeation chromatography (GPC). Table 1 provides the molecular weights of the monomodal and bimodal polymer plugs.

TABLE 1 Molecular Molecular Polydisperity Material weight (Mn) weight (Mw) (Mw/Mn) Monmodal 97200 244700 2.6 Bimodal 101200 426700 4.2

Additionally, FIGS. 1 and 2 show the molecular weight profile distributions of the monmodal and the bimodal polymer plugs. Specifically, FIG. 1 is an overlayed chromatograph showing graphs 1,2 for both the monomodal polymer plug and the bimodal polymer plug, respectively, and FIG. 2 is a chromatograph showing only the graph 2 for the bimodal polymer plug. The first peak 2 a represents the high molecular weight PLLA-co-DL material and the second peak 2 b represents the low molecular weight MLA material.

Samples of the monomodal and the bimodal plugs, described above, were placed into 14 mm diameter sawbone cavities. Each plug was heated for 15 min at 175° C. using a 4 mm diameter heating probe. In order to heat the plugs, the probe was inserted into the central opening of the stainless steel rods. The plugs were then allowed to cool after which the fixation force was measured using the following procedure:

Each sample of sawbone was placed on a cylindrical support on an Instron 5566 test machine. A rigid metal probe of 8 mm diameter, connected rigidly to a 10 kN load cell, was pressed against the one end of each of the plugs at 2 mm/min. The maximum force to push out the plug in each case was recorded and is shown in Table 2 below.

TABLE 2 Push out force (N) Bimodal plug 1 2148 2 2265 3 2880 Mean 2431 (+/−393) Monomodal plug  375  460 Mean 417 (+/−43)

Hence it can be concluded that a multi-modal polymer composition having shape memory qualities contains substantially enhanced mechanical properties compared to a monomodal shape memory polymer composition. It is believed that the enhanced mechanical properties are due to the combination of the high strength high molecular weight polymer and the flow characteristics of the low molecular weight polymer. Specifically, due to the miscibility of the polymer components, it is believed that the lower molecular weight polymer component plasticizes the higher molecular weight component. This aids flow of the multi-modal material into pores of the bone, and hence, fixation of the plug to the bone, thereby providing the plug with enhanced mechanical properties.

For the purposes of this disclosure, a multi-modal polymer composition is a polymer composition having more than one molecular weight distribution. The multi-modal composition used in this disclosure has two molecular weight distributions (bimodal), however, polymer compositions having more than two molecular weight distributions are also within the scope of this disclosure. In addition, although for the purposes of this disclosure the low molecular weight component is present at about 20% and the high molecular weight component is present at about 80%, the components may be present in any suitable proportions to give the desired increase in strength and flowability. Furthermore, the polymer blend of the present disclosure may be present as a homopolymer blend or as a co-polymer blend.

In view of the foregoing, it will be seen that the several advantages of the disclosure are achieved and attained.

The embodiments were chosen and described in order to best explain the principles of the disclosure and its practical application to thereby enable others skilled in the art to best utilize the disclosure in various embodiments and with various modifications as are suited to the particular use contemplated.

As various modifications could be made in the constructions and methods herein described and illustrated without departing from the scope of the disclosure, it is intended that all matter contained in the foregoing description or shown in the accompanying drawings shall be interpreted as illustrative rather than limiting. Thus, the breadth and scope of the present disclosure should not be limited by any of the above-described exemplary embodiments, but should be defined only in accordance with the following claims appended hereto and their equivalents. 

What is claimed is:
 1. A bone implantation article comprising a multi-modal shape memory polymer material comprising a blend of at least a first polymer component having a first molecular weight and at least a second polymer component having a second molecular weight that is less than the first component, the first polymer component and the second polymer component are miscible, at least one of the first or second polymer components are non-resorbable, and wherein upon implanting the article into bone and providing the article with energy and heating to a temperature higher than the glass transition temperature of the polymer, but lower than its melting temperature, the material flows into pores of the bone thereby enhancing fixation of the article to bone.
 2. The article of claim 1, wherein the first molecular weight is in excess of about 50,000 Daltons and the second molecular weight is up to about 20,000 Daltons.
 3. The article of claim 1, wherein the first molecular weight is between about 50,000 and about 1,000,000 Daltons and the second molecular weight is between about 2,000 and about 20,000 Daltons.
 4. The article of claim 1, wherein the first polymer component comprises about 80% of the polymer blend and the second polymer component comprises about 20% of the polymer blend.
 5. The article of claim 2, wherein the first polymer component comprises about 80% of the polymer blend and the second polymer component comprises about 20% of the polymer blend.
 6. The article of claim 1, wherein the first polymer component and the second polymer component are both non-resorbable.
 7. The article of claim 1, wherein one of the first polymer component and the second polymer component is resorbable and one of the first polymer component and the second polymer component is non-resorbable.
 8. The article of claim 1, wherein the material comprises reinforced polymeric material comprising a composite or matrix including reinforcing material or phases selected from the group consisting of glass fibers, carbon fibers, polymeric fibers, ceramic particualtes, rods, and platelets.
 9. The article of claim 1, wherein the material is porous.
 10. The article of claim 1, wherein the material comprises active agents selected from the group consisting of bone morphogenic proteins, antibiotics, anti-inflammatories, angiogenic factors, osteogenic factors, monobutyrin, thrombin, modified proteins, platelet rich plasma, platelet rich solution, platelet poor plasma, platelet poor solution, and bone marrow aspirate.
 11. The article of claim 10, wherein the active agent is incorporated into the polymeric shape memory material to be released during the relaxation and/or degradation of the polymer material.
 12. The article of claim 10, wherein the active agent combats infection and/or promotes new tissue growth at the site of implantation.
 13. The article of claim 1, wherein at least one of the first or second polymer components is selected from the group consisting of polylyacrylate, polymethyl methacrylate polymer or copolymer thereof, polybutyl methacrylate polymer or copolymer thereof, and polystyrene copolymer. 